The research results show that, those two methods were all available for above purpose, and the results measured by the two methods were identical; the real mean diameters of nanoparticles may be larger than the mean diameters measured by X-ray diffraction method, and smaller than the mean diameters measured by TEM.

采用X射线衍射法(谢乐法)与透射电子显微镜法(TEM法)对纳米粒子粒径进行测量与表征。

Using CaCO_3 nanoparticles as objects for the measurement,X-Ray Diffraction method(XRD),Transmission Electron Microscopy(TEM)and Atomic Force Microscope(AFM)were used in the measurement of CaCO_3 nanoparticles diameters.

以纳米碳酸钙粒子作为测量对象,分别采用 X 射线衍射法(XRD)、透射电子显微镜法(TEM)以及原子力显微镜法(AFM) 测量其粒径,结果表明：X 射线衍射法测量的纳米粒子粒径可能小于纳米粒子实际平均粒径,透射电子显微镜法和原子力显微镜法测量的纳米粒子粒径可能大于纳米粒子实际平均粒径。

Development of Digital Imaging System for transmission electron microscope;

透射电子显微镜数字成像系统的研制

Methods By transmission electron microscope, the structure changes about tonoplast in RP and RCAS were observed.

方法　通过透射电子显微镜对葛根和刺五加药材细胞内液泡膜的变化进行观察。

A study of the microstructures for the Al2O3 ceramic thin film in the laser -remelted area on a ZnAl - based alloy was performed by means of a transmission electron microscope associated with the techniques of optical microscope, scanning electron microscope, Auger electron spectroscope, and X ray diffraction.

用透射电子显微镜,并结合光学显微镜、扫描电子显微镜、俄歇电子能谱仪、X射线衍射等技术对锌铝基Al_2O_3陶瓷复合层激光重熔区的组织进行了分析。

8vol%TiB2 alloy with duplex structure consisting of primary equiaxed γ-grains and lamellar α2+γ colonies after creep deformation at elevated temperatures (650℃~750℃) under 250 MPa~350 MPa was studied by transmission electron microscopy (TEM).

利用透射电子显微镜对一种由等轴状γ和(γ+α2)区域组成的双态组织Ti-47Al-2Nb-2at%Mn+0。

The core/shell latex par- ticle which was characterized by transmission electron microscopy (TEM)was elucidated in detail by two categories,i.

介绍了核壳型乳胶粒子的基本形态结构和常用的表征手段,详细说明了用透射电子显微镜(TEM)表征核壳型乳胶粒子结构的两种情况,即分析透射电子显微镜法、普通透射电子显微镜法(免染色法和选择性染色法),并给出了它们的适用范围。

The sizes of SnO 2 nanocrystallines were determined by dynamic light scattering, X-ray diffraction, and computer analysis of nanocrystalline images of transmission electron microscopy.

通过动态光散射、X射线衍射和晶粒透射电子显微镜像测量 ,确定了SnO2 晶粒的线度 。

Fabrication of TEM Samples of Butted Films PLD;

透射电子显微镜对接膜样品的制作

The Study of Current-Invariable Lens Power Supply for TEM;

透射电子显微镜透镜稳流电源的研究

The observation of transmission electron microscopy(TEM) proved that the exfoliation nanocomposites were prepared.

透射电子显微镜考察表明,所制备的乙丙橡胶/OMM T纳米复合材料为剥离型结构;力学性能测试结果表明,当有机土含量仅为3份时,复合材料硫化胶的扯断强度是纯胶体系的5。

objective lens of the transmission electron microscope

透射电子显微镜物镜

high voltage transmission electron microscope

高压透射电子显微镜

bright-field transmission electron microscope

亮场透射电子显微镜

popular transmission electron microscope

普及型透射电子显微镜

transmission electron microscope laboratory

透射电子显微镜化验室

simple transmission electron microscope

简易型透射电子显微镜

scanning transmission electron microscope (STEM)

扫描透射电子显微镜

preparation of specimens for transmission electronmicroscopy

透射电子显微镜样品制备技术

Development and applications of monochromator in transmission electron microscope

透射电子显微镜单色器的发展及应用

The structure and morphology of the obtained carbon fibers are characterized by scanning electron microscopy( SEM) and transmission electron microscopy( TEM).

用扫描电子显微镜和透射电子显微镜分析了碳纤维的结构。

These features are examined by optical microscopy, scanning electron microscopy, and transmission electron microscopy.

这些图形可以用光学显微镜，扫描电子显微镜和透射电子显微镜来观察。

The morphological structure and the particle size of latex particle were studied by means of TEM.

采用透射电子显微镜研究了乳胶粒子的形态及粒径的大小。

Characteristics of H and L Subunits with Mass Spectrometry,Electrophoresis and Transmission Electron Microscopy in Liver Ferritin of Dasyatis Akajei

MALDI-TOF质谱、电泳和透射电子显微镜技术研究魟鱼肝铁蛋白H和L亚基特性

transmission scanning electron microscope

透射扫描电子显微镜

n transmission microscope

场致离子透射显微镜

EM specimen penetrator

电子显微镜标本渗透器

emission electron microscope

发射电子显微镜;发射式电子显微镜;放射电子显微镜

field emission electron microscope

场致发射电子显微镜