cvd superconducting thin film

Microwave properties of YBCO/LAO and YBCO/MgO superconducting thin films;

YBCO/LAO和YBCO/MgO超导薄膜的微波性质

Effect of Tl_2O partial pressure on component phases and properties of Tl_2Ba_2CaCu_2O_8 superconducting thin films fabricated at lower temperature in pure argon atmosphere;

低温纯Ar气中Tl_2O分压对Tl_2Ba_2CaCu_2O_8超导薄膜相组成与性能的影响

High T_c superconducting thin film of YBa_2Cu_3O_(7-x) and Zro_2 buffer layer have been de-posited in situ on(100)silicon substrate with excimer laser.

利用ＺｅＣｌ准分子激光在（１００）Ｓｉ基片上原位淀积出ＺｒＯ＿２缓冲层和ＹＢａ＿２Ｃｕ＿３Ｏ＿（７－ｘ）高Ｔ＿ｃ超导薄膜，薄膜的零电阻温度为８２Ｋ。

The results shown that the superconducting films were polycrystalline with stronger c-axis texture.

对多层蒸镀经高温退火制备的T_c≥83K的超导薄膜进行了XRD及EPMA研究。

Hollow cylindrical cathode, dc magnetron sputtering method was used to fabricate the YBCOsuperconducting films on LaAlO_3 and Zr(Y)O_2 substrate.

采用中空柱状阴极直流磁控溅射装置制备了YBCO超导薄膜。

In Situ annealed superconducting thin films are acquired by pulsed laser deposition method.

采用脉冲激光沉积的方法在Al2O3(0001)基片上先生成MgB混和薄膜,然后采用原位后退火的方法生成MgB2超导薄膜,采用磁测量(MT)、X射线衍射、扫描电子显微镜技术分析了各种沉积及退火条件对MgB2超导薄膜表面形貌、晶体结构、超导电性的影响。

The most promising application of high-TC superconducting thin films is passive microwave devices and the fabrication of large-area double-sided YBCO thin films is a convenient way to realize large scale production and multi-component integration.

YBCO高温超导薄膜在高性能微波无源器件有着良好的应用前景,而大面积双面薄膜的制备在满足批量生产及多器件集成的同时,能够进一步提高微波无源器件的性能。

The superconducting MgB2 thin films were prepared on Al2O3 polycrystalline substrates by a two-step ex-situ magnesium-diffusion method with the precursor boron thin films grown by CVD from B2H6.

以高纯乙硼烷(B2H6)为B源,采用化学气相沉积(CVD)方法在多晶Al2O3衬底上沉积B薄膜,然后在Mg蒸气中异位退火来制备MgB2超导薄膜。

Microwave measurements of the MgB_2 thin film;

MgB_2超导薄膜的微波测量